Chlorinated Polyethylene Rubber

Weifang Yaxing Chemical Co.,Ltd | Updated: Jun 27, 2017


Chlorinated Polyethylene Rubber Product Detail

Chlorinated Polyethylene Rubber.jpg


This product is a kind of irregular structure thermo elastomer without any crystals. It has the characteristic of low plastic temperature, Medium MI viscosity, fine processability,fine resistance at low temperature, fine weather resistance, fine deflection and fine fire-resistance, Not only it can be used as halide rubber solely but also it can be mixed with CR, CSM, NBR, SBR and NR at any proportion.



Tech Spec:

Items

CM135B

CM352

CM353

CM40F

CM42F

Cl Content %

35±1

35±1

35±1

40±1

42±1

Remains Crystallinity %

≤2.0

≤2.0

≤1.0

≤2.0

≤2.0

Volatile Matter Component %

≤0.4

≤0.4

≤0.4

≤0.4

≤0.4

Rate of filtration(40mesh) %

≥99

≥99

≥99

≥99

≥99

Shore Hardness A .

≤56

≤56

≤56

≤56

≤56

Tearing Strength Mpa

≥8.5

≥8.0

≥8.0

≥8.0

≥8.0

Mooney Viscosity ML(121oC,1+4)

70-80

45-65

85-100

70±5

80±5

Elongation at break %

≥800

≥800

≥800

≥800

≥800



Storage & transportation:
Kept in dry and ventilating place, avoid moisture, insolation and fire. No mix with other chemicals




PE
7130

CPE
2125

CPE
235A

CPE
1401

CPE
1402

Chlorine Content, %

35±1

35±1

30±1

25±1

35±1

40±1

40±1

Heat of fusion ,J/g

≤2.0

≤2.0

≤2.0

≤2.0

≤2.0

≤1.0

≤1.0

Shore hardness (A)

≤65

≤58

≤65

≤65

≤65

≤65

≤65

Volatile content,%

≤0.4

≤0.4

≤0.4

≤0.4

≤0.5

≤0.4

≤0.4

Tensile strength, MPa

≥8.0

≥8.0

≥8.0

≥8.0

≥6.0

≥8.0

≥8.0

Elongation at Break, %

≥700

≥700

≥700

≥700

≥600

≥700

≥700

Sieve residue(0.9mm), %

≤2.0

≤2.0

≤2.0

≤2.0

≤2.0

≤2.0

≤2.0

Bulk density, g/ml

≥0.5

≥0.5

≥0.5

≥0.5

≥0.5

≥0.5

≥0.5